Effect of gaseous carburizing thermochemical treatment on tribological behavior of Ti�6Al�4V alloy

Abstract

This study concerns the improvement of performance of resistance to wear phenomena of the Ti-6Al-4V alloy surface by means of Gaseous carburizing thermochemical treatment. Three-thermochemical treatment durations (2h, 4h, and 6h) were chosen for investigation of the effect of such treatment on this alloy. The hardness test under an indentation load of 0.05 kgf with a Vickers pyramidal indenter revealed that the surface hardness is 335 HV for the untreated samples. The hardness reaches approximately 1500 HV during gas cementation at 930 �C for variable times (2h, 4h, 6h) followed by quenching at 840 �C in an oil medium, which was accompanied by a significant improvement in wear resistance. The characterization of the modified surface layers was studied by means of a microscopic analysis and by X-ray diffraction. The case-hardening made it possible to obtain a wear resistance greater than that of the alloy not treated, minimal loss of mass by dry friction and an improvement in roughness as well as a good coefficient of friction

Keywords

• i-6al-4v
• tribological behavior
• carburizing
• wear
• hardness