Multi-Scale Numerical Simulation of Short Tungsten Fiber Reinforced Tungsten–Copper Composites: Influence Mechanisms of Fiber Parameters

Abstract

Tungsten fiber reinforced tungsten–copper (Wf/W-Cu) composites have broad application prospects in fields such as electronic packaging due to their excellent comprehensive properties. However, the correlation between fiber parameters (content, aspect ratio, orientation) and the mechanical behavior of the materials is not yet clear. In this study, a combination of numerical simulation and experimental research was employed to construct a three-dimensional microstructural mechanic model and systematically investigate the influence of fiber parameters on the tensile properties and mechanisms of Wf/W-Cu composites. The results show that: (1) The critical fiber aspect ratio is 7.6. When below this value, fiber pullout dominates, and when above this value, fiber tensile fracture is the main mechanism. (2) As the fiber content increases from 1% to 6%, the tensile strength of the composite increases by 9.6%, the yield strength increases by 10.2%, while the elongation after fracture decreases by 18.6%. (3) As the fiber orientation angle increases from 0° to 90°, the material strength first increases and then decreases, while the toughness first decreases and then increases. (4) Short fibers achieve interface toughening through fiber pullout, crack deflection, and fiber bridging, while long fibers improve the strength and toughness of the composite through load transfer and fiber bridging effects. (5) The damage evolution mechanism reveals the regulation effect of fiber parameters on the multi-scale mechanical behavior of the material. The research results can guide the composition and structure optimization design of Wf/W-Cu composites, provide new ideas for the research of high-performance fiber composites, and have important significance for their engineering applications in extreme environments.

Keywords

• W_f/W-Cu composites
• fiber parameters
• mechanical properties
• microstructural mechanics simulation
• damage evolution